PPA Amodel AT-1002 HS 产品说明:
Amodel® AT-1002 HS is a neat, toughened, heat stabilized polyphthalamide (PPA) resin that offers superior retention of properties after humid thermal aging; high impact at low temperature and better mechanical properties than many unreinforced thermoplastic polyester and nylon resins.
This material was specifically designed for automotive electrical/electronic applications such as connectors, sockets and sensors.
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
密度 | 1.13 | -- | g/cm3 | ISO 1183/A |
收缩率 | ASTM D955 | |||
流动 | 2.0 | -- | % | ASTM D955 |
横向流动 | 2.1 | -- | % | ASTM D955 |
吸水率 (24 hr) | 0.50 | -- | % | ASTM D570 |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
---|---|---|---|---|
拉伸模量 | ||||
-- | 2760 | 2760 | MPa | ASTM D638 |
23°C | 2760 | -- | MPa | ISO 527-2 |
100°C | 2100 | -- | MPa | ISO 527-2 |
拉伸应力 | ||||
屈服, 23°C | 75.2 | -- | MPa | ISO 527-2 |
屈服, 100°C | 38.6 | -- | MPa | ISO 527-2 |
断裂, 23°C | 68.3 | -- | MPa | ISO 527-2 |
-- | 83.4 | 76.5 | MPa | ASTM D638 |
拉伸应变 | ||||
屈服, 23°C | 5.0 | -- | % | ISO 527-2 |
屈服, 100°C | 3.7 | -- | % | ISO 527-2 |
断裂 1 | 80 | 100 | % | ASTM D638 |
断裂, 23°C | 15 | -- | % | ISO 527-2 |
弯曲模量 | ||||
-- | 2210 | 2280 | MPa | ASTM D790 |
23°C | 2280 | -- | MPa | ISO 178 |
100°C | 1720 | -- | MPa | ISO 178 |
PPA Amodel AT-1002 HS
聚邻苯二酰胺(简称PPA)树脂是以对苯二甲酸或邻苯二甲酸为原料的半芳香族聚酰胺。既有半结晶态的,也有非结晶态的,其玻璃化温度在255°F左右。非结晶态的PPA主要用于要求阻隔性能的场合;半结晶态的PPA树脂主要用于注塑加工,也用于其它熔融加工工艺下文主要介绍后者——半结晶态PPA树脂,特别注明的除外。半结晶态PPAS的熔点约590°F,以不透明矩形切片的形式供应。
PPA塑胶原料
:PPA荷兰DSM物性 PPA美国阿莫科物性 PPA瑞士EMS物性
(3)PPA 美阿莫科 AF-4122NL 22%玻纤增强、高光学反射能力90%以上
(4)PPA 美国阿莫科AF-1130VO 33%玻纤强化、耐高温300℃ 、良好韧性、阻燃UL94V0
(5)PPA 美国阿莫科AS-1133HS 33%玻纤强化、良好韧性、阻燃UL94HB
(6)PPA AF-4133V0 33%玻纤强化、热变形温300℃ 、良好加工性能、阻燃UL94V0
(7)PPA AF-6133V0 玻纤增强33%、适合用于红外照射和潮湿环境
(8)PPA A-1006 良好耐冲击性能、适合做承受压力的管状接头、水龙头等
(9)PPA AS-1566HS 65%矿物玻纤强化、高温高弯曲强度和硬度、可着色